| Customization: | Available |
|---|---|
| Structure Feature: | Ceramic Ball |
| Content: | >90% |
|
Still deciding? Get samples of US$ 5/kg
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
99% AL2O3 Inert Alumina Ceramic Ball - Catalyst Support Media
99% High Alumina Ceramic Ball (Catalyst Support Media) Is made from alumina powder of low silicon content.The high purity and high strength make them extremely high temperature resistance, is used to avoid the leaching reaction tower of silica cover downstream equipment or dirt or poisoned catalyst carrier.This makes them all ideal choice for support of all types of catalyst.It's widely used in petroleum, chemical, fertilizer, gas and environmental protection industries, as a catalyst in the reactor to cover support material and tower packing.It has a high temperature and high pressure resistance, bibulous rate is low, the characteristics of the chemical performance is stable.Can withstand the erosion of acid, alkali and other organic solvents, and can endure in the production process of temperature changes.Its main function is to increase gas or liquid distribution points, support and protection intensity is not high activity of the catalyst.
Chemical composition
| Al2O3 | Fe2O3 | MgO | SiO2 | Na2O | TiO2 |
| >99% | <0.1% | <0.5% | <0.2% | <0.05% | <0.05% |
| Item | Value |
| Water absorption (%) | <4 |
| Packing density (g/cm3) | 1.9-2.2 |
| Specific gravity (g/cm3) | >3.6 |
| Operation temp.(max) (ºC) | 1650 |
| Apparent porosity (%) | <1 |
| Moh's hardness (scale) | >9 |
| Acid resistance (%) | >99.6 |
| Alkali resistance (%) | >85 |
| Size | Crush strength | |
| kgf/particle | KN/particle | |
| 1/8" (3mm) | >40 | >0.4 |
| 1/4" (6mm) | >80 | >0.8 |
| 1/2" (13mm) | >580 | >5.8 |
| 3/4" (19mm) | >900 | >9.0 |
| 1" (25mm) | >1200 | >12 |
| 1-1/2"(38mm) | >1800 | >18 |
| 2" (50mm) | >2150 | >21.5 |